AWS E383 vs. N08031 Stainless Steel

Both AWS E383 and N08031 stainless steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS E383 and the bottom bar is N08031 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
210
Elongation at Break, % 34
45
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
81
Tensile Strength: Ultimate (UTS), MPa 580
730

Thermal Properties

Latent Heat of Fusion, J/g 320
310
Melting Completion (Liquidus), °C 1420
1440
Melting Onset (Solidus), °C 1370
1390
Specific Heat Capacity, J/kg-K 470
460
Thermal Conductivity, W/m-K 12
12
Thermal Expansion, µm/m-K 14
18

Otherwise Unclassified Properties

Base Metal Price, % relative 37
39
Density, g/cm3 8.1
8.1
Embodied Carbon, kg CO2/kg material 6.4
7.1
Embodied Energy, MJ/kg 89
96
Embodied Water, L/kg 240
240

Common Calculations

PREN (Pitting Resistance) 40
52
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 20
25
Strength to Weight: Bending, points 19
22
Thermal Diffusivity, mm2/s 3.1
3.1
Thermal Shock Resistance, points 15
14

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.015
Chromium (Cr), % 26.5 to 29
26 to 28
Copper (Cu), % 0.6 to 1.5
1.0 to 1.4
Iron (Fe), % 28.8 to 39.2
29 to 36.9
Manganese (Mn), % 0.5 to 2.5
0 to 2.0
Molybdenum (Mo), % 3.2 to 4.2
6.0 to 7.0
Nickel (Ni), % 30 to 33
30 to 32
Nitrogen (N), % 0
0.15 to 0.25
Phosphorus (P), % 0 to 0.020
0 to 0.020
Silicon (Si), % 0 to 0.9
0 to 0.3
Sulfur (S), % 0 to 0.020
0 to 0.010