AWS E383 vs. S32760 Stainless Steel

Both AWS E383 and S32760 stainless steel are iron alloys. They have 71% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS E383 and the bottom bar is S32760 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 34
28
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 80
80
Tensile Strength: Ultimate (UTS), MPa 580
850

Thermal Properties

Latent Heat of Fusion, J/g 320
300
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1370
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 12
15
Thermal Expansion, µm/m-K 14
13

Otherwise Unclassified Properties

Base Metal Price, % relative 37
22
Density, g/cm3 8.1
7.9
Embodied Carbon, kg CO2/kg material 6.4
4.1
Embodied Energy, MJ/kg 89
57
Embodied Water, L/kg 240
180

Common Calculations

PREN (Pitting Resistance) 40
42
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20
30
Strength to Weight: Bending, points 19
25
Thermal Diffusivity, mm2/s 3.1
4.0
Thermal Shock Resistance, points 15
23

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 26.5 to 29
24 to 26
Copper (Cu), % 0.6 to 1.5
0.5 to 1.0
Iron (Fe), % 28.8 to 39.2
57.6 to 65.8
Manganese (Mn), % 0.5 to 2.5
0 to 1.0
Molybdenum (Mo), % 3.2 to 4.2
3.0 to 4.0
Nickel (Ni), % 30 to 33
6.0 to 8.0
Nitrogen (N), % 0
0.2 to 0.3
Phosphorus (P), % 0 to 0.020
0 to 0.030
Silicon (Si), % 0 to 0.9
0 to 1.0
Sulfur (S), % 0 to 0.020
0 to 0.010
Tungsten (W), % 0
0.5 to 1.0