MakeItFrom.com
Menu (ESC)

AWS E383 vs. S41003 Stainless Steel

Both AWS E383 and S41003 stainless steel are iron alloys. They have 47% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is AWS E383 and the bottom bar is S41003 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 34
21
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
76
Tensile Strength: Ultimate (UTS), MPa 580
520

Thermal Properties

Latent Heat of Fusion, J/g 320
270
Melting Completion (Liquidus), °C 1420
1440
Melting Onset (Solidus), °C 1370
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 12
27
Thermal Expansion, µm/m-K 14
10

Otherwise Unclassified Properties

Base Metal Price, % relative 37
7.0
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.4
1.9
Embodied Energy, MJ/kg 89
27
Embodied Water, L/kg 240
97

Common Calculations

PREN (Pitting Resistance) 40
12
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20
19
Strength to Weight: Bending, points 19
18
Thermal Diffusivity, mm2/s 3.1
7.2
Thermal Shock Resistance, points 15
19

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 26.5 to 29
10.5 to 12.5
Copper (Cu), % 0.6 to 1.5
0
Iron (Fe), % 28.8 to 39.2
83.4 to 89.5
Manganese (Mn), % 0.5 to 2.5
0 to 1.5
Molybdenum (Mo), % 3.2 to 4.2
0
Nickel (Ni), % 30 to 33
0 to 1.5
Nitrogen (N), % 0
0 to 0.030
Phosphorus (P), % 0 to 0.020
0 to 0.040
Silicon (Si), % 0 to 0.9
0 to 1.0
Sulfur (S), % 0 to 0.020
0 to 0.030