AWS E385 vs. AWS E308H

Both AWS E385 and AWS E308H are iron alloys. Both are furnished in the as-welded condition. They have 78% of their average alloy composition in common.

For each property being compared, the top bar is AWS E385 and the bottom bar is AWS E308H.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
40
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
77
Tensile Strength: Ultimate (UTS), MPa 580
620

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Melting Completion (Liquidus), °C 1440
1420
Melting Onset (Solidus), °C 1390
1380
Specific Heat Capacity, J/kg-K 460
480
Thermal Conductivity, W/m-K 14
16
Thermal Expansion, µm/m-K 14
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 31
16
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 5.8
3.2
Embodied Energy, MJ/kg 79
46
Embodied Water, L/kg 200
150

Common Calculations

PREN (Pitting Resistance) 36
21
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20
22
Strength to Weight: Bending, points 19
21
Thermal Diffusivity, mm2/s 3.6
4.2
Thermal Shock Resistance, points 15
16

Alloy Composition

Carbon (C), % 0 to 0.030
0.040 to 0.080
Chromium (Cr), % 19.5 to 21.5
18 to 21
Copper (Cu), % 1.2 to 2.0
0 to 0.75
Iron (Fe), % 41.8 to 50.1
62.9 to 72.5
Manganese (Mn), % 1.0 to 2.5
0.5 to 2.5
Molybdenum (Mo), % 4.2 to 5.2
0 to 0.75
Nickel (Ni), % 24 to 26
9.0 to 11
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.9
0 to 1.0
Sulfur (S), % 0 to 0.020
0 to 0.030