AWS E385 vs. EN 1.0214 Steel

Both AWS E385 and EN 1.0214 steel are iron alloys. They have 46% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS E385 and the bottom bar is EN 1.0214 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
12 to 31
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 580
330 to 460

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Melting Completion (Liquidus), °C 1440
1470
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 460
470
Thermal Conductivity, W/m-K 14
53
Thermal Expansion, µm/m-K 14
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
6.9
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
7.9

Otherwise Unclassified Properties

Base Metal Price, % relative 31
1.8
Density, g/cm3 8.1
7.9
Embodied Carbon, kg CO2/kg material 5.8
1.4
Embodied Energy, MJ/kg 79
18
Embodied Water, L/kg 200
46

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 20
12 to 16
Strength to Weight: Bending, points 19
14 to 17
Thermal Diffusivity, mm2/s 3.6
14
Thermal Shock Resistance, points 15
11 to 14

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.060
Carbon (C), % 0 to 0.030
0.080 to 0.12
Chromium (Cr), % 19.5 to 21.5
0
Copper (Cu), % 1.2 to 2.0
0
Iron (Fe), % 41.8 to 50.1
99.17 to 99.6
Manganese (Mn), % 1.0 to 2.5
0.3 to 0.5
Molybdenum (Mo), % 4.2 to 5.2
0
Nickel (Ni), % 24 to 26
0
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 0.9
0 to 0.1
Sulfur (S), % 0 to 0.020
0 to 0.025