AWS E385 vs. EN 1.4568 Stainless Steel

Both AWS E385 and EN 1.4568 stainless steel are iron alloys. They have 71% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS E385 and the bottom bar is EN 1.4568 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
2.3 to 21
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
76
Tensile Strength: Ultimate (UTS), MPa 580
830 to 1620

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Melting Completion (Liquidus), °C 1440
1420
Melting Onset (Solidus), °C 1390
1380
Specific Heat Capacity, J/kg-K 460
480
Thermal Conductivity, W/m-K 14
16
Thermal Expansion, µm/m-K 14
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 31
13
Density, g/cm3 8.1
7.7
Embodied Carbon, kg CO2/kg material 5.8
2.8
Embodied Energy, MJ/kg 79
40
Embodied Water, L/kg 200
140

Common Calculations

PREN (Pitting Resistance) 36
17
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20
30 to 58
Strength to Weight: Bending, points 19
25 to 40
Thermal Diffusivity, mm2/s 3.6
4.3
Thermal Shock Resistance, points 15
23 to 46

Alloy Composition

Aluminum (Al), % 0
0.7 to 1.5
Carbon (C), % 0 to 0.030
0 to 0.090
Chromium (Cr), % 19.5 to 21.5
16 to 18
Copper (Cu), % 1.2 to 2.0
0
Iron (Fe), % 41.8 to 50.1
70.9 to 76.8
Manganese (Mn), % 1.0 to 2.5
0 to 1.0
Molybdenum (Mo), % 4.2 to 5.2
0
Nickel (Ni), % 24 to 26
6.5 to 7.8
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.9
0 to 0.7
Sulfur (S), % 0 to 0.020
0 to 0.015