AWS E385 vs. EN 1.4740 Stainless Steel

Both AWS E385 and EN 1.4740 stainless steel are iron alloys. They have 65% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS E385 and the bottom bar is EN 1.4740 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
22
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
77

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Melting Completion (Liquidus), °C 1440
1420
Melting Onset (Solidus), °C 1390
1370
Specific Heat Capacity, J/kg-K 460
490
Thermal Conductivity, W/m-K 14
18
Thermal Expansion, µm/m-K 14
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 31
9.5
Density, g/cm3 8.1
7.6
Embodied Carbon, kg CO2/kg material 5.8
2.3
Embodied Energy, MJ/kg 79
32
Embodied Water, L/kg 200
120

Common Calculations

PREN (Pitting Resistance) 36
18
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Thermal Diffusivity, mm2/s 3.6
4.8

Alloy Composition

Carbon (C), % 0 to 0.030
0.3 to 0.5
Chromium (Cr), % 19.5 to 21.5
16 to 19
Copper (Cu), % 1.2 to 2.0
0
Iron (Fe), % 41.8 to 50.1
75.4 to 82.7
Manganese (Mn), % 1.0 to 2.5
0 to 1.0
Molybdenum (Mo), % 4.2 to 5.2
0 to 0.5
Nickel (Ni), % 24 to 26
0 to 1.0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.9
1.0 to 2.5
Sulfur (S), % 0 to 0.020
0 to 0.030