AWS E385 vs. EN 1.5113 Steel

Both AWS E385 and EN 1.5113 steel are iron alloys. They have 48% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS E385 and the bottom bar is EN 1.5113 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
11 to 18
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
72
Tensile Strength: Ultimate (UTS), MPa 580
580 to 900

Thermal Properties

Latent Heat of Fusion, J/g 300
260
Melting Completion (Liquidus), °C 1440
1450
Melting Onset (Solidus), °C 1390
1410
Specific Heat Capacity, J/kg-K 460
480
Thermal Conductivity, W/m-K 14
52
Thermal Expansion, µm/m-K 14
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 31
2.0
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 5.8
1.4
Embodied Energy, MJ/kg 79
19
Embodied Water, L/kg 200
48

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 20
21 to 32
Strength to Weight: Bending, points 19
20 to 27
Thermal Diffusivity, mm2/s 3.6
14
Thermal Shock Resistance, points 15
17 to 26

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.1
Chromium (Cr), % 19.5 to 21.5
0
Copper (Cu), % 1.2 to 2.0
0
Iron (Fe), % 41.8 to 50.1
97 to 97.5
Manganese (Mn), % 1.0 to 2.5
1.6 to 1.8
Molybdenum (Mo), % 4.2 to 5.2
0
Nickel (Ni), % 24 to 26
0
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 0.9
0.9 to 1.1
Sulfur (S), % 0 to 0.020
0 to 0.025