MakeItFrom.com
Menu (ESC)

AWS E385 vs. EN 1.8827 Steel

Both AWS E385 and EN 1.8827 steel are iron alloys. They have 48% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS E385 and the bottom bar is EN 1.8827 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
19
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 580
610

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 460
470
Thermal Conductivity, W/m-K 14
44
Thermal Expansion, µm/m-K 14
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 31
2.6
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 5.8
1.7
Embodied Energy, MJ/kg 79
23
Embodied Water, L/kg 200
50

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 20
21
Strength to Weight: Bending, points 19
20
Thermal Diffusivity, mm2/s 3.6
12
Thermal Shock Resistance, points 15
18

Alloy Composition

Aluminum (Al), % 0
0.015 to 0.054
Carbon (C), % 0 to 0.030
0 to 0.18
Chromium (Cr), % 19.5 to 21.5
0 to 0.35
Copper (Cu), % 1.2 to 2.0
0 to 0.6
Iron (Fe), % 41.8 to 50.1
95 to 99.985
Manganese (Mn), % 1.0 to 2.5
0 to 1.8
Molybdenum (Mo), % 4.2 to 5.2
0 to 0.23
Nickel (Ni), % 24 to 26
0 to 0.85
Niobium (Nb), % 0
0 to 0.060
Nitrogen (N), % 0
0 to 0.027
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0 to 0.9
0 to 0.65
Sulfur (S), % 0 to 0.020
0 to 0.030
Titanium (Ti), % 0
0 to 0.060
Vanadium (V), % 0
0 to 0.14