AWS E385 vs. S21640 Stainless Steel

Both AWS E385 and S21640 stainless steel are iron alloys. They have 73% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS E385 and the bottom bar is S21640 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
46
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
78
Tensile Strength: Ultimate (UTS), MPa 580
740

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Melting Completion (Liquidus), °C 1440
1430
Melting Onset (Solidus), °C 1390
1380
Specific Heat Capacity, J/kg-K 460
480
Thermal Conductivity, W/m-K 14
15
Thermal Expansion, µm/m-K 14
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 31
17
Density, g/cm3 8.1
7.7
Embodied Carbon, kg CO2/kg material 5.8
3.6
Embodied Energy, MJ/kg 79
51
Embodied Water, L/kg 200
150

Common Calculations

PREN (Pitting Resistance) 36
26
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20
27
Strength to Weight: Bending, points 19
23
Thermal Diffusivity, mm2/s 3.6
4.0
Thermal Shock Resistance, points 15
16

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.080
Chromium (Cr), % 19.5 to 21.5
17.5 to 19.5
Copper (Cu), % 1.2 to 2.0
0
Iron (Fe), % 41.8 to 50.1
63 to 74.3
Manganese (Mn), % 1.0 to 2.5
3.5 to 6.5
Molybdenum (Mo), % 4.2 to 5.2
0.5 to 2.0
Nickel (Ni), % 24 to 26
4.0 to 6.5
Niobium (Nb), % 0
0.1 to 1.0
Nitrogen (N), % 0
0.080 to 0.3
Phosphorus (P), % 0 to 0.030
0 to 0.060
Silicon (Si), % 0 to 0.9
0 to 1.0
Sulfur (S), % 0 to 0.020
0 to 0.030