AWS E410 vs. Grade N7M Nickel

AWS E410 belongs to the iron alloys classification, while grade N7M nickel belongs to the nickel alloys. There are 23 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS E410 and the bottom bar is grade N7M nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
220
Elongation at Break, % 23
22
Poisson's Ratio 0.28
0.31
Shear Modulus, GPa 76
85
Tensile Strength: Ultimate (UTS), MPa 580
590
Tensile Strength: Yield (Proof), MPa 440
310

Thermal Properties

Latent Heat of Fusion, J/g 270
320
Melting Completion (Liquidus), °C 1450
1650
Melting Onset (Solidus), °C 1400
1590
Specific Heat Capacity, J/kg-K 480
390
Thermal Expansion, µm/m-K 14
9.9

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
75
Density, g/cm3 7.8
9.3
Embodied Carbon, kg CO2/kg material 2.0
16
Embodied Energy, MJ/kg 28
200
Embodied Water, L/kg 100
270

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
110
Resilience: Unit (Modulus of Resilience), kJ/m3 500
220
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
22
Strength to Weight: Axial, points 21
18
Strength to Weight: Bending, points 20
17
Thermal Shock Resistance, points 16
19

Alloy Composition

Carbon (C), % 0 to 0.12
0 to 0.070
Chromium (Cr), % 11 to 13.5
0 to 1.0
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 82.2 to 89
0 to 3.0
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 0 to 0.75
30 to 33
Nickel (Ni), % 0 to 0.7
60.9 to 70
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 0.9
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030