AWS E430Nb vs. AISI 410S Stainless Steel

Both AWS E430Nb and AISI 410S stainless steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS E430Nb and the bottom bar is AISI 410S stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 23
25
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
76
Tensile Strength: Ultimate (UTS), MPa 500
480

Thermal Properties

Latent Heat of Fusion, J/g 280
270
Melting Completion (Liquidus), °C 1450
1440
Melting Onset (Solidus), °C 1410
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 24
30
Thermal Expansion, µm/m-K 14
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.6
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 15
7.0
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 3.1
1.9
Embodied Energy, MJ/kg 45
27
Embodied Water, L/kg 120
100

Common Calculations

PREN (Pitting Resistance) 18
13
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18
17
Strength to Weight: Bending, points 18
18
Thermal Diffusivity, mm2/s 6.6
8.1
Thermal Shock Resistance, points 13
17

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.080
Chromium (Cr), % 15 to 18
11.5 to 13.5
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 76.2 to 84.5
83.8 to 88.5
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 0 to 0.75
0
Nickel (Ni), % 0 to 0.6
0 to 0.6
Niobium (Nb), % 0.5 to 1.5
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030