AWS E430Nb vs. EN 1.7323 Steel

Both AWS E430Nb and EN 1.7323 steel are iron alloys. They have 82% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AWS E430Nb and the bottom bar is EN 1.7323 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 500
480 to 1460

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 24
45
Thermal Expansion, µm/m-K 14
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.6
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 15
2.5
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 3.1
1.5
Embodied Energy, MJ/kg 45
20
Embodied Water, L/kg 120
50

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
17 to 52
Strength to Weight: Bending, points 18
17 to 36
Thermal Diffusivity, mm2/s 6.6
12
Thermal Shock Resistance, points 13
14 to 43

Alloy Composition

Carbon (C), % 0 to 0.1
0.17 to 0.23
Chromium (Cr), % 15 to 18
0.3 to 0.6
Copper (Cu), % 0 to 0.75
0 to 0.25
Iron (Fe), % 76.2 to 84.5
97.1 to 98.4
Manganese (Mn), % 0 to 1.0
0.7 to 1.0
Molybdenum (Mo), % 0 to 0.75
0.4 to 0.5
Nickel (Ni), % 0 to 0.6
0
Niobium (Nb), % 0.5 to 1.5
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0 to 0.030
0.020 to 0.040