AWS E70C-B2L vs. AWS E3155

Both AWS E70C-B2L and AWS E3155 are iron alloys. They have a modest 33% of their average alloy composition in common, which, by itself, doesn't mean much. There are 23 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AWS E70C-B2L and the bottom bar is AWS E3155.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 21
23
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
81
Tensile Strength: Ultimate (UTS), MPa 580
770

Thermal Properties

Latent Heat of Fusion, J/g 260
310
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
450
Thermal Conductivity, W/m-K 39
13
Thermal Expansion, µm/m-K 13
13

Otherwise Unclassified Properties

Base Metal Price, % relative 3.0
70
Density, g/cm3 7.8
8.4
Embodied Carbon, kg CO2/kg material 1.6
7.7
Embodied Energy, MJ/kg 22
110
Embodied Water, L/kg 54
300

Common Calculations

PREN (Pitting Resistance) 3.0
35
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 20
26
Strength to Weight: Bending, points 20
22
Thermal Diffusivity, mm2/s 11
3.3
Thermal Shock Resistance, points 17
20

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0 to 0.050
0 to 0.1
Chromium (Cr), % 1.0 to 1.5
20 to 22.5
Cobalt (Co), % 0
18.5 to 21
Copper (Cu), % 0 to 0.35
0 to 0.75
Iron (Fe), % 95.1 to 98
23.3 to 36.3
Manganese (Mn), % 0.4 to 1.0
1.0 to 2.5
Molybdenum (Mo), % 0.4 to 0.65
2.5 to 3.5
Nickel (Ni), % 0 to 0.2
19 to 21
Niobium (Nb), % 0
0.75 to 1.3
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0.25 to 0.6
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0
2.0 to 3.0
Vanadium (V), % 0 to 0.030
0
Residuals, % 0 to 0.5
0