AWS E70C-B2L vs. SAE-AISI 1211 Steel

Both AWS E70C-B2L and SAE-AISI 1211 steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is AWS E70C-B2L and the bottom bar is SAE-AISI 1211 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 21
11 to 29
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 580
430 to 580
Tensile Strength: Yield (Proof), MPa 460
260 to 460

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
52
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 3.0
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.6
1.4
Embodied Energy, MJ/kg 22
18
Embodied Water, L/kg 54
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
61 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 550
180 to 550
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 20
15 to 21
Strength to Weight: Bending, points 20
16 to 20
Thermal Diffusivity, mm2/s 11
14
Thermal Shock Resistance, points 17
14 to 18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0 to 0.050
0 to 0.13
Chromium (Cr), % 1.0 to 1.5
0
Copper (Cu), % 0 to 0.35
0
Iron (Fe), % 95.1 to 98
98.7 to 99.23
Manganese (Mn), % 0.4 to 1.0
0.6 to 0.9
Molybdenum (Mo), % 0.4 to 0.65
0
Nickel (Ni), % 0 to 0.2
0
Phosphorus (P), % 0 to 0.025
0.070 to 0.12
Silicon (Si), % 0.25 to 0.6
0
Sulfur (S), % 0 to 0.030
0.1 to 0.15
Vanadium (V), % 0 to 0.030
0
Residuals, % 0 to 0.5
0