AWS E80C-B2 vs. AISI 445 Stainless Steel

Both AWS E80C-B2 and AISI 445 stainless steel are iron alloys. They have 80% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is AWS E80C-B2 and the bottom bar is AISI 445 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 22
25
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Tensile Strength: Ultimate (UTS), MPa 630
480
Tensile Strength: Yield (Proof), MPa 530
230

Thermal Properties

Latent Heat of Fusion, J/g 260
290
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 39
21
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
2.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
3.0

Otherwise Unclassified Properties

Base Metal Price, % relative 3.0
12
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.6
2.6
Embodied Energy, MJ/kg 22
38
Embodied Water, L/kg 53
130

Common Calculations

PREN (Pitting Resistance) 3.0
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
98
Resilience: Unit (Modulus of Resilience), kJ/m3 740
140
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22
17
Strength to Weight: Bending, points 21
18
Thermal Diffusivity, mm2/s 11
5.6
Thermal Shock Resistance, points 18
16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0.050 to 0.12
0 to 0.020
Chromium (Cr), % 1.0 to 1.5
19 to 21
Copper (Cu), % 0
0.3 to 0.6
Iron (Fe), % 95.3 to 97.9
74.9 to 80.7
Manganese (Mn), % 0.4 to 1.0
0 to 1.0
Molybdenum (Mo), % 0.4 to 0.65
0
Nickel (Ni), % 0 to 0.2
0 to 0.6
Niobium (Nb), % 0
0 to 0.8
Nitrogen (N), % 0
0 to 0.030
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0.25 to 0.6
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.012
Vanadium (V), % 0 to 0.030
0
Residuals, % 0 to 0.5
0