AWS E80C-B2 vs. AWS E2593

Both AWS E80C-B2 and AWS E2593 are iron alloys. They have 61% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AWS E80C-B2 and the bottom bar is AWS E2593.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 22
17
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
80
Tensile Strength: Ultimate (UTS), MPa 630
850

Thermal Properties

Latent Heat of Fusion, J/g 260
300
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
16
Thermal Expansion, µm/m-K 13
14

Otherwise Unclassified Properties

Base Metal Price, % relative 3.0
22
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
4.2
Embodied Energy, MJ/kg 22
59
Embodied Water, L/kg 53
190

Common Calculations

PREN (Pitting Resistance) 3.0
39
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22
30
Strength to Weight: Bending, points 21
25
Thermal Diffusivity, mm2/s 11
4.3
Thermal Shock Resistance, points 18
21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0.050 to 0.12
0 to 0.040
Chromium (Cr), % 1.0 to 1.5
24 to 27
Copper (Cu), % 0
1.5 to 3.0
Iron (Fe), % 95.3 to 97.9
52.7 to 62.5
Manganese (Mn), % 0.4 to 1.0
0.5 to 1.5
Molybdenum (Mo), % 0.4 to 0.65
2.9 to 3.9
Nickel (Ni), % 0 to 0.2
8.5 to 10.5
Nitrogen (N), % 0
0.080 to 0.25
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0.25 to 0.6
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Vanadium (V), % 0 to 0.030
0
Residuals, % 0 to 0.5
0