AWS E80C-B2 or E55C-B2 (W52030) Weld Metal
AWS E80C-B2 is a weld metal formulated for joining alloy steels. Cited properties are appropriate for the post-weld heat treated (PWHT) condition. E80C-B2 is the AWS designation for this material. W52030 is the UNS number.
It has a moderately low thermal conductivity and a moderately low base cost among alloy steel welding fillers.
The graph bars on the material properties cards below compare AWS E80C-B2 to: alloy steel welding fillers (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
190 GPa 27 x 106 psi
Elongation at Break
22 %
Poisson's Ratio
0.29
Shear Modulus
73 GPa 11 x 106 psi
Tensile Strength: Ultimate (UTS)
630 MPa 91 x 103 psi
Tensile Strength: Yield (Proof)
530 MPa 76 x 103 psi
Thermal Properties
Latent Heat of Fusion
260 J/g
Melting Completion (Liquidus)
1460 °C 2660 °F
Melting Onset (Solidus)
1420 °C 2580 °F
Specific Heat Capacity
470 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
39 W/m-K 23 BTU/h-ft-°F
Thermal Expansion
13 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
7.5 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.6 % IACS
Otherwise Unclassified Properties
Base Metal Price
3.0 % relative
Density
7.8 g/cm3 490 lb/ft3
Embodied Carbon
1.6 kg CO2/kg material
Embodied Energy
22 MJ/kg 9.3 x 103 BTU/lb
Embodied Water
53 L/kg 6.3 gal/lb
Common Calculations
PREN (Pitting Resistance)
3.0
Resilience: Ultimate (Unit Rupture Work)
130 MJ/m3
Resilience: Unit (Modulus of Resilience)
740 kJ/m3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
22 points
Strength to Weight: Bending
21 points
Thermal Diffusivity
11 mm2/s
Thermal Shock Resistance
18 points
Alloy Composition
| Fe | 95.3 to 97.9 | |
| Cr | 1.0 to 1.5 | |
| Mn | 0.4 to 1.0 | |
| Mo | 0.4 to 0.65 | |
| Si | 0.25 to 0.6 | |
| Ni | 0 to 0.2 | |
| C | 0.050 to 0.12 | |
| S | 0 to 0.030 | |
| V | 0 to 0.030 | |
| P | 0 to 0.025 | |
| res. | 0 to 0.5 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Similar Alloys
Further Reading
AWS A5.28: Specification for Low-Alloy Steel Electrodes and Rods for Gas Shielded Arc Welding
Welding Metallurgy, 2nd ed., Sindo Kou, 2003