AWS E80C-B2 vs. EN 1.4971 Stainless Steel
Both AWS E80C-B2 and EN 1.4971 stainless steel are iron alloys. They have a modest 34% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is AWS E80C-B2 and the bottom bar is EN 1.4971 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Elongation at Break, % | 22 | |
| 34 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 630 | |
| 800 |
| Tensile Strength: Yield (Proof), MPa | 530 | |
| 340 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 300 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 450 |
| Thermal Conductivity, W/m-K | 39 | |
| 13 |
| Thermal Expansion, µm/m-K | 13 | |
| 15 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 3.0 | |
| 70 |
| Density, g/cm3 | 7.8 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 7.6 |
| Embodied Energy, MJ/kg | 22 | |
| 110 |
| Embodied Water, L/kg | 53 | |
| 300 |
Common Calculations
| PREN (Pitting Resistance) | 3.0 | |
| 38 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 | |
| 220 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 740 | |
| 280 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 22 | |
| 26 |
| Strength to Weight: Bending, points | 21 | |
| 23 |
| Thermal Diffusivity, mm2/s | 11 | |
| 3.4 |
| Thermal Shock Resistance, points | 18 | |
| 19 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0.050 to 0.12 | |
| 0.080 to 0.16 |
| Chromium (Cr), % | 1.0 to 1.5 | |
| 20 to 22.5 |
| Cobalt (Co), % | 0 | |
| 18.5 to 21 |
| Iron (Fe), % | 95.3 to 97.9 | |
| 24.3 to 37.1 |
| Manganese (Mn), % | 0.4 to 1.0 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0.4 to 0.65 | |
| 2.5 to 3.5 |
| Nickel (Ni), % | 0 to 0.2 | |
| 19 to 21 |
| Niobium (Nb), % | 0 | |
| 0.75 to 1.3 |
| Nitrogen (N), % | 0 | |
| 0.1 to 0.2 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.035 |
| Silicon (Si), % | 0.25 to 0.6 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |
| Tungsten (W), % | 0 | |
| 2.0 to 3.0 |
| Vanadium (V), % | 0 to 0.030 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |