AWS E80C-B2 vs. EN 1.7701 Steel

Both AWS E80C-B2 and EN 1.7701 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS E80C-B2 and the bottom bar is EN 1.7701 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 630
670 to 2010

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
44
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 3.0
2.6
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
1.9
Embodied Energy, MJ/kg 22
26
Embodied Water, L/kg 53
52

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 22
24 to 71
Strength to Weight: Bending, points 21
22 to 45
Thermal Diffusivity, mm2/s 11
12
Thermal Shock Resistance, points 18
20 to 59

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0.050 to 0.12
0.48 to 0.56
Chromium (Cr), % 1.0 to 1.5
0.9 to 1.2
Iron (Fe), % 95.3 to 97.9
96.2 to 97.7
Manganese (Mn), % 0.4 to 1.0
0.7 to 1.1
Molybdenum (Mo), % 0.4 to 0.65
0.15 to 0.3
Nickel (Ni), % 0 to 0.2
0
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0.25 to 0.6
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.025
Vanadium (V), % 0 to 0.030
0.1 to 0.2
Residuals, % 0 to 0.5
0