AWS E80C-B2 vs. EN 1.8827 Steel

Both AWS E80C-B2 and EN 1.8827 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is AWS E80C-B2 and the bottom bar is EN 1.8827 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 22
19
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 630
610
Tensile Strength: Yield (Proof), MPa 530
440

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
44
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 3.0
2.6
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
1.7
Embodied Energy, MJ/kg 22
23
Embodied Water, L/kg 53
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
110
Resilience: Unit (Modulus of Resilience), kJ/m3 740
510
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 22
21
Strength to Weight: Bending, points 21
20
Thermal Diffusivity, mm2/s 11
12
Thermal Shock Resistance, points 18
18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0.015 to 0.054
Carbon (C), % 0.050 to 0.12
0 to 0.18
Chromium (Cr), % 1.0 to 1.5
0 to 0.35
Copper (Cu), % 0
0 to 0.6
Iron (Fe), % 95.3 to 97.9
95 to 99.985
Manganese (Mn), % 0.4 to 1.0
0 to 1.8
Molybdenum (Mo), % 0.4 to 0.65
0 to 0.23
Nickel (Ni), % 0 to 0.2
0 to 0.85
Niobium (Nb), % 0
0 to 0.060
Nitrogen (N), % 0
0 to 0.027
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0.25 to 0.6
0 to 0.65
Sulfur (S), % 0 to 0.030
0 to 0.030
Titanium (Ti), % 0
0 to 0.060
Vanadium (V), % 0 to 0.030
0 to 0.14
Residuals, % 0 to 0.5
0