AWS E80C-B2 vs. SAE-AISI M62 Steel

Both AWS E80C-B2 and SAE-AISI M62 steel are iron alloys. They have 78% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS E80C-B2 and the bottom bar is SAE-AISI M62 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
79
Tensile Strength: Ultimate (UTS), MPa 630
830 to 2440

Thermal Properties

Latent Heat of Fusion, J/g 260
260
Melting Completion (Liquidus), °C 1460
1650
Melting Onset (Solidus), °C 1420
1600
Specific Heat Capacity, J/kg-K 470
430
Thermal Expansion, µm/m-K 13
12

Otherwise Unclassified Properties

Base Metal Price, % relative 3.0
30
Density, g/cm3 7.8
8.5
Embodied Carbon, kg CO2/kg material 1.6
10
Embodied Energy, MJ/kg 22
150
Embodied Water, L/kg 53
110

Common Calculations

PREN (Pitting Resistance) 3.0
49
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 22
27 to 80
Strength to Weight: Bending, points 21
23 to 47
Thermal Shock Resistance, points 18
24 to 71

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0.050 to 0.12
1.3 to 1.4
Chromium (Cr), % 1.0 to 1.5
3.5 to 4.0
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 95.3 to 97.9
73.6 to 77.4
Manganese (Mn), % 0.4 to 1.0
0.15 to 0.4
Molybdenum (Mo), % 0.4 to 0.65
10 to 11
Nickel (Ni), % 0 to 0.2
0 to 0.3
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0.25 to 0.6
0.15 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0
5.8 to 6.5
Vanadium (V), % 0 to 0.030
1.8 to 2.1
Residuals, % 0 to 0.5
0