MakeItFrom.com
Menu (ESC)

AWS E80C-B2 vs. N08811 Stainless Steel

Both AWS E80C-B2 and N08811 stainless steel are iron alloys. They have 48% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AWS E80C-B2 and the bottom bar is N08811 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 22
33
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 630
510
Tensile Strength: Yield (Proof), MPa 530
190

Thermal Properties

Latent Heat of Fusion, J/g 260
300
Melting Completion (Liquidus), °C 1460
1390
Melting Onset (Solidus), °C 1420
1360
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 39
12
Thermal Expansion, µm/m-K 13
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 3.0
30
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 1.6
5.3
Embodied Energy, MJ/kg 22
76
Embodied Water, L/kg 53
200

Common Calculations

PREN (Pitting Resistance) 3.0
21
Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
130
Resilience: Unit (Modulus of Resilience), kJ/m3 740
94
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 22
18
Strength to Weight: Bending, points 21
18
Thermal Diffusivity, mm2/s 11
3.0
Thermal Shock Resistance, points 18
13

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0.15 to 0.6
Carbon (C), % 0.050 to 0.12
0.060 to 0.1
Chromium (Cr), % 1.0 to 1.5
19 to 23
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 95.3 to 97.9
39.5 to 50.6
Manganese (Mn), % 0.4 to 1.0
0 to 1.5
Molybdenum (Mo), % 0.4 to 0.65
0
Nickel (Ni), % 0 to 0.2
30 to 35
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0.25 to 0.6
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
0.15 to 0.6
Vanadium (V), % 0 to 0.030
0
Residuals, % 0 to 0.5
0