AWS E80C-B2 vs. S40930 Stainless Steel

Both AWS E80C-B2 and S40930 stainless steel are iron alloys. They have 89% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is AWS E80C-B2 and the bottom bar is S40930 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 22
23
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
75
Tensile Strength: Ultimate (UTS), MPa 630
430
Tensile Strength: Yield (Proof), MPa 530
190

Thermal Properties

Latent Heat of Fusion, J/g 260
270
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 39
25
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 3.0
8.5
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
2.3
Embodied Energy, MJ/kg 22
32
Embodied Water, L/kg 53
94

Common Calculations

PREN (Pitting Resistance) 3.0
11
Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
80
Resilience: Unit (Modulus of Resilience), kJ/m3 740
94
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22
16
Strength to Weight: Bending, points 21
16
Thermal Diffusivity, mm2/s 11
6.7
Thermal Shock Resistance, points 18
16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0.050 to 0.12
0 to 0.030
Chromium (Cr), % 1.0 to 1.5
10.5 to 11.7
Iron (Fe), % 95.3 to 97.9
84.7 to 89.4
Manganese (Mn), % 0.4 to 1.0
0 to 1.0
Molybdenum (Mo), % 0.4 to 0.65
0
Nickel (Ni), % 0 to 0.2
0 to 0.5
Niobium (Nb), % 0
0.080 to 0.75
Nitrogen (N), % 0
0 to 0.030
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0.25 to 0.6
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.020
Titanium (Ti), % 0
0.050 to 0.2
Vanadium (V), % 0 to 0.030
0
Residuals, % 0 to 0.5
0