AWS E80C-Ni1 vs. S15500 Stainless Steel
Both AWS E80C-Ni1 and S15500 stainless steel are iron alloys. They have 78% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is AWS E80C-Ni1 and the bottom bar is S15500 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 27 | |
| 6.8 to 16 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 72 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 890 to 1490 |
| Tensile Strength: Yield (Proof), MPa | 540 | |
| 590 to 1310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 280 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1430 |
| Melting Onset (Solidus), °C | 1420 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 40 | |
| 17 |
| Thermal Expansion, µm/m-K | 13 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
| 2.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
| 2.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.6 | |
| 13 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 2.7 |
| Embodied Energy, MJ/kg | 21 | |
| 39 |
| Embodied Water, L/kg | 49 | |
| 130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 160 | |
| 98 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 770 | |
| 890 to 4460 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 22 | |
| 32 to 53 |
| Strength to Weight: Bending, points | 21 | |
| 26 to 37 |
| Thermal Diffusivity, mm2/s | 11 | |
| 4.6 |
| Thermal Shock Resistance, points | 18 | |
| 30 to 50 |
Alloy Composition
| Carbon (C), % | 0 to 0.12 | |
| 0 to 0.070 |
| Chromium (Cr), % | 0 | |
| 14 to 15.5 |
| Copper (Cu), % | 0 to 0.35 | |
| 2.5 to 4.5 |
| Iron (Fe), % | 95.1 to 99.2 | |
| 71.9 to 79.9 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 to 0.3 | |
| 0 |
| Nickel (Ni), % | 0.8 to 1.1 | |
| 3.5 to 5.5 |
| Niobium (Nb), % | 0 | |
| 0.15 to 0.45 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.9 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Vanadium (V), % | 0 to 0.030 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |