AWS ENiCrFe-2 vs. EN 1.7710 Steel
AWS ENiCrFe-2 belongs to the nickel alloys classification, while EN 1.7710 steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is AWS ENiCrFe-2 and the bottom bar is EN 1.7710 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 28 | |
| 6.8 to 11 |
| Poisson's Ratio | 0.3 | |
| 0.29 |
| Shear Modulus, GPa | 74 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 790 | |
| 930 to 1070 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 260 |
| Melting Completion (Liquidus), °C | 1390 | |
| 1470 |
| Melting Onset (Solidus), °C | 1350 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 65 | |
| 3.5 |
| Density, g/cm3 | 8.5 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 11 | |
| 2.2 |
| Embodied Energy, MJ/kg | 160 | |
| 30 |
| Embodied Water, L/kg | 260 | |
| 57 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 26 | |
| 33 to 38 |
| Strength to Weight: Bending, points | 22 | |
| 27 to 30 |
| Thermal Shock Resistance, points | 24 | |
| 27 to 31 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 to 0.1 | |
| 0.12 to 0.18 |
| Chromium (Cr), % | 13 to 17 | |
| 1.3 to 1.8 |
| Cobalt (Co), % | 0 to 0.12 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 |
| Iron (Fe), % | 0 to 12 | |
| 95.1 to 97 |
| Manganese (Mn), % | 1.0 to 3.5 | |
| 0.6 to 1.0 |
| Molybdenum (Mo), % | 0.5 to 2.5 | |
| 0.8 to 1.0 |
| Nickel (Ni), % | 62 to 85 | |
| 0 |
| Niobium (Nb), % | 0.5 to 4.0 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.75 | |
| 0 to 0.6 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.030 |
| Vanadium (V), % | 0 | |
| 0.15 to 0.25 |
| Residuals, % | 0 to 0.5 | |
| 0 |