AWS ENiCrMo-4 vs. Grade 360 Molybdenum
AWS ENiCrMo-4 belongs to the nickel alloys classification, while grade 360 molybdenum belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is AWS ENiCrMo-4 and the bottom bar is grade 360 molybdenum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 310 |
| Elongation at Break, % | 28 | |
| 6.3 to 17 |
| Poisson's Ratio | 0.29 | |
| 0.31 |
| Shear Modulus, GPa | 84 | |
| 120 |
| Tensile Strength: Ultimate (UTS), MPa | 790 | |
| 430 to 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 370 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 250 |
| Thermal Expansion, µm/m-K | 12 | |
| 7.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.0 | |
| 10 |
| Embodied Carbon, kg CO2/kg material | 13 | |
| 28 |
| Embodied Energy, MJ/kg | 170 | |
| 330 |
| Embodied Water, L/kg | 280 | |
| 360 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 17 |
| Stiffness to Weight: Bending, points | 22 | |
| 22 |
| Strength to Weight: Axial, points | 24 | |
| 12 to 17 |
| Strength to Weight: Bending, points | 21 | |
| 12 to 16 |
| Thermal Shock Resistance, points | 22 | |
| 14 to 21 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 to 0.020 | |
| 0 to 0.030 |
| Chromium (Cr), % | 14.5 to 16.5 | |
| 0 |
| Cobalt (Co), % | 0 to 2.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 |
| Iron (Fe), % | 4.0 to 7.0 | |
| 0 to 0.010 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 |
| Molybdenum (Mo), % | 15 to 17 | |
| 99.9 to 100 |
| Nickel (Ni), % | 49.9 to 63.5 | |
| 0 to 0.0020 |
| Nitrogen (N), % | 0 | |
| 0 to 0.0020 |
| Oxygen (O), % | 0 | |
| 0 to 0.0015 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 to 0.010 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tungsten (W), % | 3.0 to 4.5 | |
| 0 |
| Vanadium (V), % | 0 to 0.35 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |