AWS ER80S-B3L vs. ASTM B780 Alloy

AWS ER80S-B3L belongs to the iron alloys classification, while ASTM B780 alloy belongs to the otherwise unclassified metals. There are 16 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is AWS ER80S-B3L and the bottom bar is ASTM B780 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
83
Elongation at Break, % 19
1.1 to 9.1
Poisson's Ratio 0.29
0.36
Shear Modulus, GPa 74
30
Tensile Strength: Ultimate (UTS), MPa 630
330 to 590

Thermal Properties

Latent Heat of Fusion, J/g 260
140
Specific Heat Capacity, J/kg-K 470
270
Thermal Expansion, µm/m-K 13
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.7
70 to 76
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
62 to 68

Otherwise Unclassified Properties

Density, g/cm3 7.8
10

Common Calculations

Stiffness to Weight: Axial, points 13
4.5
Stiffness to Weight: Bending, points 24
14
Strength to Weight: Axial, points 22
9.1 to 16
Strength to Weight: Bending, points 21
11 to 15
Thermal Shock Resistance, points 18
16 to 29

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Cadmium (Cd), % 0
0 to 0.050
Carbon (C), % 0 to 0.050
0
Chromium (Cr), % 2.3 to 2.7
0
Copper (Cu), % 0 to 0.35
23.5 to 25.7
Iron (Fe), % 93.6 to 96
0 to 0.050
Lead (Pb), % 0
0 to 0.030
Manganese (Mn), % 0.4 to 0.7
0
Molybdenum (Mo), % 0.9 to 1.2
0
Nickel (Ni), % 0 to 0.2
0.35 to 0.65
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0.4 to 0.7
0
Silver (Ag), % 0
74 to 76
Sulfur (S), % 0 to 0.025
0
Zinc (Zn), % 0
0 to 0.060
Residuals, % 0 to 0.5
0