AWS ER80S-B3L vs. AWS E316H

Both AWS ER80S-B3L and AWS E316H are iron alloys. They have 69% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AWS ER80S-B3L and the bottom bar is AWS E316H.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 19
34
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
78
Tensile Strength: Ultimate (UTS), MPa 630
580

Thermal Properties

Latent Heat of Fusion, J/g 260
290
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 41
15
Thermal Expansion, µm/m-K 13
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.7
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 4.1
20
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.8
4.0
Embodied Energy, MJ/kg 23
55
Embodied Water, L/kg 60
160

Common Calculations

PREN (Pitting Resistance) 6.0
27
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22
21
Strength to Weight: Bending, points 21
20
Thermal Diffusivity, mm2/s 11
4.0
Thermal Shock Resistance, points 18
15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0 to 0.050
0.040 to 0.080
Chromium (Cr), % 2.3 to 2.7
17 to 20
Copper (Cu), % 0 to 0.35
0 to 0.75
Iron (Fe), % 93.6 to 96
58.6 to 69.5
Manganese (Mn), % 0.4 to 0.7
0.5 to 2.5
Molybdenum (Mo), % 0.9 to 1.2
2.0 to 3.0
Nickel (Ni), % 0 to 0.2
11 to 14
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0.4 to 0.7
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030
Residuals, % 0 to 0.5
0