AWS ER80S-B3L vs. EN 1.0348 Steel

Both AWS ER80S-B3L and EN 1.0348 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is AWS ER80S-B3L and the bottom bar is EN 1.0348 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19
28
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Tensile Strength: Ultimate (UTS), MPa 630
380
Tensile Strength: Yield (Proof), MPa 530
220

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 41
50
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.7
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 4.1
2.1
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.8
1.5
Embodied Energy, MJ/kg 23
19
Embodied Water, L/kg 60
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
91
Resilience: Unit (Modulus of Resilience), kJ/m3 730
130
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 22
13
Strength to Weight: Bending, points 21
15
Thermal Diffusivity, mm2/s 11
13
Thermal Shock Resistance, points 18
12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0.020 to 0.2
Carbon (C), % 0 to 0.050
0 to 0.13
Chromium (Cr), % 2.3 to 2.7
0 to 0.3
Copper (Cu), % 0 to 0.35
0 to 0.3
Iron (Fe), % 93.6 to 96
97.5 to 99.98
Manganese (Mn), % 0.4 to 0.7
0 to 0.7
Molybdenum (Mo), % 0.9 to 1.2
0 to 0.080
Nickel (Ni), % 0 to 0.2
0 to 0.3
Niobium (Nb), % 0
0 to 0.010
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0.4 to 0.7
0 to 0.35
Sulfur (S), % 0 to 0.025
0 to 0.010
Titanium (Ti), % 0
0 to 0.040
Vanadium (V), % 0
0 to 0.020
Residuals, % 0 to 0.5
0