AWS ER80S-B3L vs. EN 1.4841 Stainless Steel

Both AWS ER80S-B3L and EN 1.4841 stainless steel are iron alloys. They have 55% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AWS ER80S-B3L and the bottom bar is EN 1.4841 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 19
32
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
78
Tensile Strength: Ultimate (UTS), MPa 630
650
Tensile Strength: Yield (Proof), MPa 530
260

Thermal Properties

Latent Heat of Fusion, J/g 260
330
Melting Completion (Liquidus), °C 1460
1380
Melting Onset (Solidus), °C 1420
1340
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 41
15
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.7
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
2.2

Otherwise Unclassified Properties

Base Metal Price, % relative 4.1
25
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.8
4.3
Embodied Energy, MJ/kg 23
62
Embodied Water, L/kg 60
190

Common Calculations

PREN (Pitting Resistance) 6.0
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
170
Resilience: Unit (Modulus of Resilience), kJ/m3 730
170
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22
23
Strength to Weight: Bending, points 21
21
Thermal Diffusivity, mm2/s 11
4.0
Thermal Shock Resistance, points 18
15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0 to 0.050
0 to 0.2
Chromium (Cr), % 2.3 to 2.7
24 to 26
Copper (Cu), % 0 to 0.35
0
Iron (Fe), % 93.6 to 96
47.1 to 55.5
Manganese (Mn), % 0.4 to 0.7
0 to 2.0
Molybdenum (Mo), % 0.9 to 1.2
0
Nickel (Ni), % 0 to 0.2
19 to 22
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0.4 to 0.7
1.5 to 2.5
Sulfur (S), % 0 to 0.025
0 to 0.015
Residuals, % 0 to 0.5
0