AWS ER80S-B3L vs. C67400 Bronze
AWS ER80S-B3L belongs to the iron alloys classification, while C67400 bronze belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is AWS ER80S-B3L and the bottom bar is C67400 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 19 | |
| 22 to 28 |
| Poisson's Ratio | 0.29 | |
| 0.31 |
| Shear Modulus, GPa | 74 | |
| 41 |
| Tensile Strength: Ultimate (UTS), MPa | 630 | |
| 480 to 610 |
| Tensile Strength: Yield (Proof), MPa | 530 | |
| 250 to 370 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 190 |
| Melting Completion (Liquidus), °C | 1460 | |
| 890 |
| Melting Onset (Solidus), °C | 1420 | |
| 870 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 400 |
| Thermal Conductivity, W/m-K | 41 | |
| 100 |
| Thermal Expansion, µm/m-K | 13 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.7 | |
| 23 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.9 | |
| 26 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 4.1 | |
| 23 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.8 | |
| 2.8 |
| Embodied Energy, MJ/kg | 23 | |
| 48 |
| Embodied Water, L/kg | 60 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 | |
| 110 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 730 | |
| 300 to 660 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 24 | |
| 20 |
| Strength to Weight: Axial, points | 22 | |
| 17 to 22 |
| Strength to Weight: Bending, points | 21 | |
| 17 to 20 |
| Thermal Diffusivity, mm2/s | 11 | |
| 32 |
| Thermal Shock Resistance, points | 18 | |
| 16 to 20 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0.5 to 2.0 |
| Carbon (C), % | 0 to 0.050 | |
| 0 |
| Chromium (Cr), % | 2.3 to 2.7 | |
| 0 |
| Copper (Cu), % | 0 to 0.35 | |
| 57 to 60 |
| Iron (Fe), % | 93.6 to 96 | |
| 0 to 0.35 |
| Lead (Pb), % | 0 | |
| 0 to 0.5 |
| Manganese (Mn), % | 0.4 to 0.7 | |
| 2.0 to 3.5 |
| Molybdenum (Mo), % | 0.9 to 1.2 | |
| 0 |
| Nickel (Ni), % | 0 to 0.2 | |
| 0 to 0.25 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0.4 to 0.7 | |
| 0.5 to 1.5 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.3 |
| Zinc (Zn), % | 0 | |
| 31.1 to 40 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |