Both AWS ER80S-B3L and K93600 alloy are iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS ER80S-B3L and the bottom bar is K93600 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
140
Elongation at Break, % 19
5.0 to 35
Tensile Strength: Ultimate (UTS), MPa 630
480 to 810
Tensile Strength: Yield (Proof), MPa 530
280 to 750

Thermal Properties

Melting Onset (Solidus), °C 1420
1430
Specific Heat Capacity, J/kg-K 470
520
Thermal Conductivity, W/m-K 41
13
Thermal Expansion, µm/m-K 13
7.3

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.7
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
2.4

Otherwise Unclassified Properties

Density, g/cm3 7.8
8.1

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
21 to 280
Resilience: Unit (Modulus of Resilience), kJ/m3 730
280 to 2050
Stiffness to Weight: Axial, points 13
9.4
Stiffness to Weight: Bending, points 24
21
Strength to Weight: Axial, points 22
16 to 28
Strength to Weight: Bending, points 21
17 to 24
Thermal Diffusivity, mm2/s 11
3.1
Thermal Shock Resistance, points 18
34 to 57