AWS ER80S-B3L vs. R60706 Alloy

AWS ER80S-B3L belongs to the iron alloys classification, while R60706 alloy belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS ER80S-B3L and the bottom bar is R60706 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
98
Elongation at Break, % 19
16
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 74
37
Tensile Strength: Ultimate (UTS), MPa 630
580
Tensile Strength: Yield (Proof), MPa 530
390

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Specific Heat Capacity, J/kg-K 470
270
Thermal Conductivity, W/m-K 41
17
Thermal Expansion, µm/m-K 13
6.3

Otherwise Unclassified Properties

Density, g/cm3 7.8
6.7
Embodied Water, L/kg 60
450

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
82
Resilience: Unit (Modulus of Resilience), kJ/m3 730
760
Stiffness to Weight: Axial, points 13
8.1
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 22
24
Strength to Weight: Bending, points 21
23
Thermal Diffusivity, mm2/s 11
9.5
Thermal Shock Resistance, points 18
67

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0 to 0.050
0 to 0.050
Chromium (Cr), % 2.3 to 2.7
0 to 0.2
Copper (Cu), % 0 to 0.35
0
Hafnium (Hf), % 0
0 to 4.5
Hydrogen (H), % 0
0 to 0.0050
Iron (Fe), % 93.6 to 96
0 to 0.2
Manganese (Mn), % 0.4 to 0.7
0
Molybdenum (Mo), % 0.9 to 1.2
0
Nickel (Ni), % 0 to 0.2
0
Niobium (Nb), % 0
2.0 to 3.0
Nitrogen (N), % 0
0 to 0.025
Oxygen (O), % 0
0 to 0.16
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0.4 to 0.7
0
Sulfur (S), % 0 to 0.025
0
Zirconium (Zr), % 0
91 to 98
Residuals, % 0 to 0.5
0