AWS ER80S-B3L vs. S41041 Stainless Steel

Both AWS ER80S-B3L and S41041 stainless steel are iron alloys. They have 90% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS ER80S-B3L and the bottom bar is S41041 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19
17
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
76
Tensile Strength: Ultimate (UTS), MPa 630
910
Tensile Strength: Yield (Proof), MPa 530
580

Thermal Properties

Latent Heat of Fusion, J/g 260
270
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 41
29
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.7
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 4.1
8.5
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.8
2.2
Embodied Energy, MJ/kg 23
31
Embodied Water, L/kg 60
100

Common Calculations

PREN (Pitting Resistance) 6.0
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
140
Resilience: Unit (Modulus of Resilience), kJ/m3 730
860
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22
32
Strength to Weight: Bending, points 21
27
Thermal Diffusivity, mm2/s 11
7.8
Thermal Shock Resistance, points 18
33

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0 to 0.050
0.13 to 0.18
Chromium (Cr), % 2.3 to 2.7
11.5 to 13
Copper (Cu), % 0 to 0.35
0
Iron (Fe), % 93.6 to 96
84.5 to 87.8
Manganese (Mn), % 0.4 to 0.7
0.4 to 0.6
Molybdenum (Mo), % 0.9 to 1.2
0 to 0.2
Nickel (Ni), % 0 to 0.2
0 to 0.5
Niobium (Nb), % 0
0.15 to 0.45
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0.4 to 0.7
0 to 0.5
Sulfur (S), % 0 to 0.025
0 to 0.030
Residuals, % 0 to 0.5
0