AWS ER80S-B3L vs. Z41321 Zinc

AWS ER80S-B3L belongs to the iron alloys classification, while Z41321 zinc belongs to the zinc alloys. There are 27 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AWS ER80S-B3L and the bottom bar is Z41321 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
87
Elongation at Break, % 19
60
Poisson's Ratio 0.29
0.25
Shear Modulus, GPa 74
35
Tensile Strength: Ultimate (UTS), MPa 630
190
Tensile Strength: Yield (Proof), MPa 530
150

Thermal Properties

Latent Heat of Fusion, J/g 260
110
Melting Completion (Liquidus), °C 1460
410
Melting Onset (Solidus), °C 1420
400
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 41
110
Thermal Expansion, µm/m-K 13
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.7
27
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
37

Otherwise Unclassified Properties

Base Metal Price, % relative 4.1
12
Density, g/cm3 7.8
6.6
Embodied Carbon, kg CO2/kg material 1.8
2.8
Embodied Energy, MJ/kg 23
54
Embodied Water, L/kg 60
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
100
Resilience: Unit (Modulus of Resilience), kJ/m3 730
130
Stiffness to Weight: Axial, points 13
7.4
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 22
7.9
Strength to Weight: Bending, points 21
11
Thermal Diffusivity, mm2/s 11
44
Thermal Shock Resistance, points 18
5.9

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.010
Cadmium (Cd), % 0
0 to 0.0050
Carbon (C), % 0 to 0.050
0
Chromium (Cr), % 2.3 to 2.7
0
Copper (Cu), % 0 to 0.35
0.5 to 1.0
Iron (Fe), % 93.6 to 96
0 to 0.010
Lead (Pb), % 0
0 to 0.010
Manganese (Mn), % 0.4 to 0.7
0
Molybdenum (Mo), % 0.9 to 1.2
0
Nickel (Ni), % 0 to 0.2
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0.4 to 0.7
0
Sulfur (S), % 0 to 0.025
0
Tin (Sn), % 0
0 to 0.0030
Titanium (Ti), % 0
0.080 to 0.18
Zinc (Zn), % 0
98.8 to 99.42
Residuals, % 0 to 0.5
0