MakeItFrom.com
Menu (ESC)

AWS ER90S-B3 vs. AWS ER100S-1

Both AWS ER90S-B3 and AWS ER100S-1 are iron alloys. They have a very high 97% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is AWS ER90S-B3 and the bottom bar is AWS ER100S-1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19
18
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 690
770
Tensile Strength: Yield (Proof), MPa 620
700

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
49
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.7
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 4.1
3.6
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.8
1.8
Embodied Energy, MJ/kg 24
24
Embodied Water, L/kg 60
54

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
130
Resilience: Unit (Modulus of Resilience), kJ/m3 1000
1290
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25
27
Strength to Weight: Bending, points 22
24
Thermal Diffusivity, mm2/s 11
13
Thermal Shock Resistance, points 20
23

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.1
Carbon (C), % 0.070 to 0.12
0 to 0.080
Chromium (Cr), % 2.3 to 2.7
0 to 0.3
Copper (Cu), % 0 to 0.35
0 to 0.25
Iron (Fe), % 93.5 to 95.9
93.5 to 96.9
Manganese (Mn), % 0.4 to 0.7
1.3 to 1.8
Molybdenum (Mo), % 0.9 to 1.2
0.25 to 0.55
Nickel (Ni), % 0 to 0.2
1.4 to 2.1
Phosphorus (P), % 0 to 0.025
0 to 0.010
Silicon (Si), % 0.4 to 0.7
0.2 to 0.55
Sulfur (S), % 0 to 0.025
0 to 0.010
Titanium (Ti), % 0
0 to 0.1
Vanadium (V), % 0
0 to 0.050
Zirconium (Zr), % 0
0 to 0.1
Residuals, % 0 to 0.5
0 to 0.5