AWS ER90S-B3 vs. EN 1.7365 Steel

Both AWS ER90S-B3 and EN 1.7365 steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AWS ER90S-B3 and the bottom bar is EN 1.7365 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19
18
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
74
Tensile Strength: Ultimate (UTS), MPa 690
700
Tensile Strength: Yield (Proof), MPa 620
470

Thermal Properties

Latent Heat of Fusion, J/g 260
260
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
40
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.7
8.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
9.4

Otherwise Unclassified Properties

Base Metal Price, % relative 4.1
4.4
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.8
1.8
Embodied Energy, MJ/kg 24
24
Embodied Water, L/kg 60
70

Common Calculations

PREN (Pitting Resistance) 6.0
6.8
Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
110
Resilience: Unit (Modulus of Resilience), kJ/m3 1000
580
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 25
25
Strength to Weight: Bending, points 22
22
Thermal Diffusivity, mm2/s 11
11
Thermal Shock Resistance, points 20
20

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0.070 to 0.12
0.12 to 0.19
Chromium (Cr), % 2.3 to 2.7
4.0 to 6.0
Copper (Cu), % 0 to 0.35
0 to 0.3
Iron (Fe), % 93.5 to 95.9
91.2 to 94.9
Manganese (Mn), % 0.4 to 0.7
0.5 to 0.8
Molybdenum (Mo), % 0.9 to 1.2
0.45 to 0.65
Nickel (Ni), % 0 to 0.2
0
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0.4 to 0.7
0 to 0.8
Sulfur (S), % 0 to 0.025
0 to 0.025
Vanadium (V), % 0
0 to 0.050
Residuals, % 0 to 0.5
0