AWS ER90S-B3 vs. N08135 Stainless Steel

Both AWS ER90S-B3 and N08135 stainless steel are iron alloys. They have 41% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS ER90S-B3 and the bottom bar is N08135 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 19
46
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
80
Tensile Strength: Ultimate (UTS), MPa 690
570
Tensile Strength: Yield (Proof), MPa 620
240

Thermal Properties

Latent Heat of Fusion, J/g 260
310
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
460
Thermal Expansion, µm/m-K 13
16

Otherwise Unclassified Properties

Base Metal Price, % relative 4.1
39
Density, g/cm3 7.8
8.2
Embodied Carbon, kg CO2/kg material 1.8
6.8
Embodied Energy, MJ/kg 24
94
Embodied Water, L/kg 60
220

Common Calculations

PREN (Pitting Resistance) 6.0
38
Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
210
Resilience: Unit (Modulus of Resilience), kJ/m3 1000
140
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25
19
Strength to Weight: Bending, points 22
19
Thermal Shock Resistance, points 20
13

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0.070 to 0.12
0 to 0.030
Chromium (Cr), % 2.3 to 2.7
20.5 to 23.5
Copper (Cu), % 0 to 0.35
0 to 0.7
Iron (Fe), % 93.5 to 95.9
30.2 to 42.3
Manganese (Mn), % 0.4 to 0.7
0 to 1.0
Molybdenum (Mo), % 0.9 to 1.2
4.0 to 5.0
Nickel (Ni), % 0 to 0.2
33 to 38
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0.4 to 0.7
0 to 0.75
Sulfur (S), % 0 to 0.025
0 to 0.030
Tungsten (W), % 0
0.2 to 0.8
Residuals, % 0 to 0.5
0