AWS ERNiCrCoMo-1 vs. AISI 302 Stainless Steel

AWS ERNiCrCoMo-1 belongs to the nickel alloys classification, while AISI 302 stainless steel belongs to the iron alloys. They have a modest 29% of their average alloy composition in common, which, by itself, doesn't mean much. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrCoMo-1 and the bottom bar is AISI 302 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 28
4.5 to 46
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 81
77
Tensile Strength: Ultimate (UTS), MPa 710
580 to 1430

Thermal Properties

Latent Heat of Fusion, J/g 330
280
Melting Completion (Liquidus), °C 1420
1420
Melting Onset (Solidus), °C 1370
1400
Specific Heat Capacity, J/kg-K 450
480
Thermal Conductivity, W/m-K 13
16
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 75
15
Density, g/cm3 8.5
7.8
Embodied Carbon, kg CO2/kg material 10
3.0
Embodied Energy, MJ/kg 140
42
Embodied Water, L/kg 350
140

Common Calculations

Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 23
21 to 51
Strength to Weight: Bending, points 21
20 to 36
Thermal Diffusivity, mm2/s 3.5
4.4
Thermal Shock Resistance, points 19
12 to 31

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0.8 to 1.5
0
Carbon (C), % 0.050 to 0.15
0 to 0.15
Chromium (Cr), % 20 to 24
17 to 19
Cobalt (Co), % 10 to 15
0
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 0 to 3.0
67.9 to 75
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 8.0 to 10
0
Nickel (Ni), % 42.7 to 61.2
8.0 to 10
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 0.75
Sulfur (S), % 0 to 0.015
0 to 0.030
Titanium (Ti), % 0 to 0.6
0
Residuals, % 0 to 0.5
0