AWS ERNiCrCoMo-1 vs. EN 1.4600 Stainless Steel

AWS ERNiCrCoMo-1 belongs to the nickel alloys classification, while EN 1.4600 stainless steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrCoMo-1 and the bottom bar is EN 1.4600 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 28
23
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 81
76
Tensile Strength: Ultimate (UTS), MPa 710
580

Thermal Properties

Latent Heat of Fusion, J/g 330
270
Melting Completion (Liquidus), °C 1420
1440
Melting Onset (Solidus), °C 1370
1400
Specific Heat Capacity, J/kg-K 450
480
Thermal Conductivity, W/m-K 13
27
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
3.4

Otherwise Unclassified Properties

Base Metal Price, % relative 75
7.0
Density, g/cm3 8.5
7.7
Embodied Carbon, kg CO2/kg material 10
2.0
Embodied Energy, MJ/kg 140
28
Embodied Water, L/kg 350
100

Common Calculations

Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 23
21
Strength to Weight: Bending, points 21
20
Thermal Diffusivity, mm2/s 3.5
7.3
Thermal Shock Resistance, points 19
21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0.8 to 1.5
0
Carbon (C), % 0.050 to 0.15
0 to 0.030
Chromium (Cr), % 20 to 24
11 to 13
Cobalt (Co), % 10 to 15
0
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 0 to 3.0
82 to 87.7
Manganese (Mn), % 0 to 1.0
1.0 to 2.5
Molybdenum (Mo), % 8.0 to 10
0
Nickel (Ni), % 42.7 to 61.2
0.3 to 1.0
Nitrogen (N), % 0
0 to 0.025
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.015
Titanium (Ti), % 0 to 0.6
0 to 0.35
Residuals, % 0 to 0.5
0