AWS ERNiCrCoMo-1 vs. EN 1.4669 Stainless Steel

AWS ERNiCrCoMo-1 belongs to the nickel alloys classification, while EN 1.4669 stainless steel belongs to the iron alloys. They have a modest 27% of their average alloy composition in common, which, by itself, doesn't mean much. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrCoMo-1 and the bottom bar is EN 1.4669 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 28
28
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 81
78
Tensile Strength: Ultimate (UTS), MPa 710
780

Thermal Properties

Latent Heat of Fusion, J/g 330
290
Melting Completion (Liquidus), °C 1420
1420
Melting Onset (Solidus), °C 1370
1370
Specific Heat Capacity, J/kg-K 450
480
Thermal Conductivity, W/m-K 13
15
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 75
13
Density, g/cm3 8.5
7.7
Embodied Carbon, kg CO2/kg material 10
2.6
Embodied Energy, MJ/kg 140
38
Embodied Water, L/kg 350
160

Common Calculations

Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 23
28
Strength to Weight: Bending, points 21
24
Thermal Diffusivity, mm2/s 3.5
4.0
Thermal Shock Resistance, points 19
21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0.8 to 1.5
0
Carbon (C), % 0.050 to 0.15
0 to 0.045
Chromium (Cr), % 20 to 24
21.5 to 24
Cobalt (Co), % 10 to 15
0
Copper (Cu), % 0 to 0.5
1.6 to 3.0
Iron (Fe), % 0 to 3.0
65.2 to 74.8
Manganese (Mn), % 0 to 1.0
1.0 to 3.0
Molybdenum (Mo), % 8.0 to 10
0 to 0.5
Nickel (Ni), % 42.7 to 61.2
1.0 to 3.0
Nitrogen (N), % 0
0.12 to 0.2
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.030
Titanium (Ti), % 0 to 0.6
0
Residuals, % 0 to 0.5
0