AWS ERNiCrCoMo-1 vs. EN 1.7220 Steel

AWS ERNiCrCoMo-1 belongs to the nickel alloys classification, while EN 1.7220 steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrCoMo-1 and the bottom bar is EN 1.7220 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 81
73
Tensile Strength: Ultimate (UTS), MPa 710
520 to 1720

Thermal Properties

Latent Heat of Fusion, J/g 330
250
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 13
44
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 75
2.5
Density, g/cm3 8.5
7.8
Embodied Carbon, kg CO2/kg material 10
1.5
Embodied Energy, MJ/kg 140
20
Embodied Water, L/kg 350
51

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 23
18 to 61
Strength to Weight: Bending, points 21
18 to 41
Thermal Diffusivity, mm2/s 3.5
12
Thermal Shock Resistance, points 19
15 to 50

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0.8 to 1.5
0
Carbon (C), % 0.050 to 0.15
0.3 to 0.37
Chromium (Cr), % 20 to 24
0.9 to 1.2
Cobalt (Co), % 10 to 15
0
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 0 to 3.0
96.8 to 98.1
Manganese (Mn), % 0 to 1.0
0.6 to 0.9
Molybdenum (Mo), % 8.0 to 10
0.15 to 0.3
Nickel (Ni), % 42.7 to 61.2
0
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.015
0 to 0.035
Titanium (Ti), % 0 to 0.6
0
Residuals, % 0 to 0.5
0