MakeItFrom.com
Menu (ESC)

AWS ERNiCrCoMo-1 vs. EN 1.7375 Steel

AWS ERNiCrCoMo-1 belongs to the nickel alloys classification, while EN 1.7375 steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrCoMo-1 and the bottom bar is EN 1.7375 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 28
20
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 81
74
Tensile Strength: Ultimate (UTS), MPa 710
620

Thermal Properties

Latent Heat of Fusion, J/g 330
250
Melting Completion (Liquidus), °C 1420
1470
Melting Onset (Solidus), °C 1370
1430
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 13
39
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 75
3.9
Density, g/cm3 8.5
7.9
Embodied Carbon, kg CO2/kg material 10
1.8
Embodied Energy, MJ/kg 140
23
Embodied Water, L/kg 350
59

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 23
22
Strength to Weight: Bending, points 21
20
Thermal Diffusivity, mm2/s 3.5
11
Thermal Shock Resistance, points 19
18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0.8 to 1.5
0.010 to 0.040
Carbon (C), % 0.050 to 0.15
0.1 to 0.15
Chromium (Cr), % 20 to 24
2.0 to 2.5
Cobalt (Co), % 10 to 15
0
Copper (Cu), % 0 to 0.5
0 to 0.25
Iron (Fe), % 0 to 3.0
94.5 to 96.7
Manganese (Mn), % 0 to 1.0
0.3 to 0.8
Molybdenum (Mo), % 8.0 to 10
0.9 to 1.1
Nickel (Ni), % 42.7 to 61.2
0 to 0.3
Nitrogen (N), % 0
0 to 0.012
Phosphorus (P), % 0 to 0.030
0 to 0.015
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0 to 0.015
0 to 0.010
Titanium (Ti), % 0 to 0.6
0
Residuals, % 0 to 0.5
0