AWS ERNiCrCoMo-1 vs. EN AC-46600 Aluminum

AWS ERNiCrCoMo-1 belongs to the nickel alloys classification, while EN AC-46600 aluminum belongs to the aluminum alloys. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AWS ERNiCrCoMo-1 and the bottom bar is EN AC-46600 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
72
Elongation at Break, % 28
1.1
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 81
27
Tensile Strength: Ultimate (UTS), MPa 710
180

Thermal Properties

Latent Heat of Fusion, J/g 330
490
Melting Completion (Liquidus), °C 1420
620
Melting Onset (Solidus), °C 1370
560
Specific Heat Capacity, J/kg-K 450
890
Thermal Conductivity, W/m-K 13
130
Thermal Expansion, µm/m-K 13
22

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
29
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
94

Otherwise Unclassified Properties

Base Metal Price, % relative 75
10
Density, g/cm3 8.5
2.8
Embodied Carbon, kg CO2/kg material 10
7.8
Embodied Energy, MJ/kg 140
150
Embodied Water, L/kg 350
1080

Common Calculations

Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 23
50
Strength to Weight: Axial, points 23
18
Strength to Weight: Bending, points 21
25
Thermal Diffusivity, mm2/s 3.5
51
Thermal Shock Resistance, points 19
8.1

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0.8 to 1.5
85.6 to 92.4
Carbon (C), % 0.050 to 0.15
0
Chromium (Cr), % 20 to 24
0
Cobalt (Co), % 10 to 15
0
Copper (Cu), % 0 to 0.5
1.5 to 2.5
Iron (Fe), % 0 to 3.0
0 to 0.8
Lead (Pb), % 0
0 to 0.25
Magnesium (Mg), % 0
0 to 0.35
Manganese (Mn), % 0 to 1.0
0.15 to 0.65
Molybdenum (Mo), % 8.0 to 10
0
Nickel (Ni), % 42.7 to 61.2
0 to 0.35
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0 to 1.0
6.0 to 8.0
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
0 to 0.15
Titanium (Ti), % 0 to 0.6
0 to 0.25
Zinc (Zn), % 0
0 to 1.0
Residuals, % 0 to 0.5
0 to 0.15