AWS ERNiCrCoMo-1 vs. Grade 350 Maraging Steel
AWS ERNiCrCoMo-1 belongs to the nickel alloys classification, while grade 350 maraging steel belongs to the iron alloys. They have a modest 37% of their average alloy composition in common, which, by itself, doesn't mean much. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is AWS ERNiCrCoMo-1 and the bottom bar is grade 350 maraging steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Elongation at Break, % | 28 | |
| 4.1 to 18 |
| Poisson's Ratio | 0.29 | |
| 0.3 |
| Shear Modulus, GPa | 81 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 710 | |
| 1140 to 2420 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 270 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1470 |
| Melting Onset (Solidus), °C | 1370 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 450 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 75 | |
| 39 |
| Density, g/cm3 | 8.5 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 10 | |
| 5.6 |
| Embodied Energy, MJ/kg | 140 | |
| 74 |
| Embodied Water, L/kg | 350 | |
| 160 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 23 |
| Strength to Weight: Axial, points | 23 | |
| 38 to 82 |
| Strength to Weight: Bending, points | 21 | |
| 29 to 49 |
| Thermal Shock Resistance, points | 19 | |
| 35 to 74 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0.8 to 1.5 | |
| 0.050 to 0.15 |
| Boron (B), % | 0 | |
| 0 to 0.0030 |
| Calcium (Ca), % | 0 | |
| 0 to 0.050 |
| Carbon (C), % | 0.050 to 0.15 | |
| 0 to 0.030 |
| Chromium (Cr), % | 20 to 24 | |
| 0 |
| Cobalt (Co), % | 10 to 15 | |
| 11.5 to 12.5 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 |
| Iron (Fe), % | 0 to 3.0 | |
| 61.2 to 64.6 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 0.1 |
| Molybdenum (Mo), % | 8.0 to 10 | |
| 4.6 to 5.2 |
| Nickel (Ni), % | 42.7 to 61.2 | |
| 18 to 19 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 to 0.6 | |
| 1.3 to 1.6 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.020 |
| Residuals, % | 0 to 0.5 | |
| 0 |