AWS ERNiCrCoMo-1 vs. SAE-AISI 1213 Steel

AWS ERNiCrCoMo-1 belongs to the nickel alloys classification, while SAE-AISI 1213 steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrCoMo-1 and the bottom bar is SAE-AISI 1213 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 28
11 to 29
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 81
73
Tensile Strength: Ultimate (UTS), MPa 710
440 to 600

Thermal Properties

Latent Heat of Fusion, J/g 330
250
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 13
51
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 75
1.8
Density, g/cm3 8.5
7.8
Embodied Carbon, kg CO2/kg material 10
1.4
Embodied Energy, MJ/kg 140
18
Embodied Water, L/kg 350
46

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 23
16 to 21
Strength to Weight: Bending, points 21
17 to 20
Thermal Diffusivity, mm2/s 3.5
14
Thermal Shock Resistance, points 19
14 to 19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0.8 to 1.5
0
Carbon (C), % 0.050 to 0.15
0 to 0.13
Chromium (Cr), % 20 to 24
0
Cobalt (Co), % 10 to 15
0
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 0 to 3.0
98.4 to 99
Manganese (Mn), % 0 to 1.0
0.7 to 1.0
Molybdenum (Mo), % 8.0 to 10
0
Nickel (Ni), % 42.7 to 61.2
0
Phosphorus (P), % 0 to 0.030
0.070 to 0.12
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.015
0.24 to 0.33
Titanium (Ti), % 0 to 0.6
0
Residuals, % 0 to 0.5
0