AWS ERNiCrCoMo-1 vs. SAE-AISI H26 Steel

AWS ERNiCrCoMo-1 belongs to the nickel alloys classification, while SAE-AISI H26 steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrCoMo-1 and the bottom bar is SAE-AISI H26 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
210
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 81
80
Tensile Strength: Ultimate (UTS), MPa 710
720 to 2100

Thermal Properties

Latent Heat of Fusion, J/g 330
240
Melting Completion (Liquidus), °C 1420
1810
Melting Onset (Solidus), °C 1370
1760
Specific Heat Capacity, J/kg-K 450
410
Thermal Conductivity, W/m-K 13
22
Thermal Expansion, µm/m-K 13
12

Otherwise Unclassified Properties

Base Metal Price, % relative 75
45
Density, g/cm3 8.5
9.3
Embodied Carbon, kg CO2/kg material 10
8.1
Embodied Energy, MJ/kg 140
120
Embodied Water, L/kg 350
90

Common Calculations

Stiffness to Weight: Axial, points 14
12
Stiffness to Weight: Bending, points 23
21
Strength to Weight: Axial, points 23
22 to 63
Strength to Weight: Bending, points 21
19 to 39
Thermal Diffusivity, mm2/s 3.5
5.6
Thermal Shock Resistance, points 19
22 to 63

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0.8 to 1.5
0
Carbon (C), % 0.050 to 0.15
0.45 to 0.55
Chromium (Cr), % 20 to 24
3.8 to 4.5
Cobalt (Co), % 10 to 15
0
Copper (Cu), % 0 to 0.5
0 to 0.25
Iron (Fe), % 0 to 3.0
73.3 to 77.5
Manganese (Mn), % 0 to 1.0
0.15 to 0.4
Molybdenum (Mo), % 8.0 to 10
0
Nickel (Ni), % 42.7 to 61.2
0 to 0.3
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0 to 1.0
0.15 to 0.4
Sulfur (S), % 0 to 0.015
0 to 0.030
Titanium (Ti), % 0 to 0.6
0
Tungsten (W), % 0
17.3 to 19
Vanadium (V), % 0
0.75 to 1.3
Residuals, % 0 to 0.5
0