AWS ERNiCrCoMo-1 vs. SAE-AISI M47 Steel

AWS ERNiCrCoMo-1 belongs to the nickel alloys classification, while SAE-AISI M47 steel belongs to the iron alloys. They have a modest 20% of their average alloy composition in common, which, by itself, doesn't mean much. There are 21 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrCoMo-1 and the bottom bar is SAE-AISI M47 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 81
77
Tensile Strength: Ultimate (UTS), MPa 710
810 to 2310

Thermal Properties

Latent Heat of Fusion, J/g 330
270
Melting Completion (Liquidus), °C 1420
1540
Melting Onset (Solidus), °C 1370
1500
Specific Heat Capacity, J/kg-K 450
450
Thermal Conductivity, W/m-K 13
23
Thermal Expansion, µm/m-K 13
11

Otherwise Unclassified Properties

Base Metal Price, % relative 75
26
Density, g/cm3 8.5
8.1
Embodied Carbon, kg CO2/kg material 10
7.4
Embodied Energy, MJ/kg 140
100
Embodied Water, L/kg 350
120

Common Calculations

Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 23
28 to 79
Strength to Weight: Bending, points 21
24 to 48
Thermal Diffusivity, mm2/s 3.5
6.3
Thermal Shock Resistance, points 19
27 to 77

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0.8 to 1.5
0
Carbon (C), % 0.050 to 0.15
1.1 to 1.2
Chromium (Cr), % 20 to 24
3.5 to 4.0
Cobalt (Co), % 10 to 15
4.8 to 5.3
Copper (Cu), % 0 to 0.5
0 to 0.25
Iron (Fe), % 0 to 3.0
78.7 to 85
Manganese (Mn), % 0 to 1.0
0.15 to 0.4
Molybdenum (Mo), % 8.0 to 10
9.3 to 10
Nickel (Ni), % 42.7 to 61.2
0 to 0.3
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0 to 1.0
0.2 to 0.45
Sulfur (S), % 0 to 0.015
0 to 0.030
Titanium (Ti), % 0 to 0.6
0
Tungsten (W), % 0
1.3 to 1.8
Vanadium (V), % 0
1.2 to 1.4
Residuals, % 0 to 0.5
0