AWS ERNiCrCoMo-1 vs. N06255 Nickel
Both AWS ERNiCrCoMo-1 and N06255 nickel are nickel alloys. They have 82% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is AWS ERNiCrCoMo-1 and the bottom bar is N06255 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 210 |
| Elongation at Break, % | 28 | |
| 45 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 81 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 710 | |
| 660 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 320 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1470 |
| Melting Onset (Solidus), °C | 1370 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 450 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 75 | |
| 55 |
| Density, g/cm3 | 8.5 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 10 | |
| 9.4 |
| Embodied Energy, MJ/kg | 140 | |
| 130 |
| Embodied Water, L/kg | 350 | |
| 270 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 23 |
| Strength to Weight: Axial, points | 23 | |
| 22 |
| Strength to Weight: Bending, points | 21 | |
| 20 |
| Thermal Shock Resistance, points | 19 | |
| 17 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0.8 to 1.5 | |
| 0 |
| Carbon (C), % | 0.050 to 0.15 | |
| 0 to 0.030 |
| Chromium (Cr), % | 20 to 24 | |
| 23 to 26 |
| Cobalt (Co), % | 10 to 15 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 to 1.2 |
| Iron (Fe), % | 0 to 3.0 | |
| 6.0 to 24 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 8.0 to 10 | |
| 6.0 to 9.0 |
| Nickel (Ni), % | 42.7 to 61.2 | |
| 47 to 52 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0 to 0.6 | |
| 0 to 0.69 |
| Tungsten (W), % | 0 | |
| 0 to 3.0 |
| Residuals, % | 0 to 0.5 | |
| 0 |